Aluminum extrusion power amplifier case metal products aluminum shell CNC processing

Aluminum extrusion power amplifier case metal products aluminum shell CNC processing

  • Material
    AL6063
  • Finished
    Sandblasting Anodic Oxidation
  • Color
    Silver/red/black/colorful
  • Salt Spray Test
    96 H
  • Tolerance
    ISO2768FH
  • Process
    Cnc Machining, Turning CNC Parts, CNC Milling, Turning, According To The Workpiece And Precision
  • Place of Origin
    China Shenzhen
  • Brand Name
    Tec-Key
  • Minimum Order Quantity
    100 pcs
  • Price
    USD0.5-30 pcs
  • Packaging Details
    32*23*17cm
  • Delivery Time
    5-8 work days
  • Payment Terms
    T/T
  • Supply Ability
    10000 pcs days

Aluminum extrusion power amplifier case metal products aluminum shell CNC processing

Aluminum extrusion power amplifier case metal products aluminum shell CNC processing

 

Scope
Aluminium alloy 6063 is a medium strength alloy commonly referred to as an architectural alloy.It is normally used in intricate extrusions.It has a good surface finish, high corrosion resistance, is suited to welding and can be easily anodised.Most commonly available as T6 temper, in the T4 condition it has good formability.
 
Application
This material is used for architectural applications, shop fittings, irrigation tubing, balustrading, window frames,3C cooling parts, Decorative metal panels,mechanical parts, automobile parts, outdoor fitness equipment. extrusions and doors.
 
Supplied Forms
1 Extrusions
2 Tube
3 sheet material
 
Alloy Designations
Aluminium alloy 6063/6063A also corresponds to: AA6063, Al Mg0.7Si, GS10, AlMgSi0.5, A-GS, 3.32206, ASTM B210, ASTM B221, ASTM B241(pipe-seamless), ASTM B345 (pipe-seamless), ASTM B361, ASTM B429, ASTM B483, ASTM B491, MIL G-18014, MIL G-18015, MIL P-25995,MIL W-85, QQ A-200/9, SAE J454, UNS A96063 and HE19.
 
Temper Types
The most common tempers for 6063 aluminium are: O - Soft, T4-Solution heat treated and naturally aged to a substantially stable condition andT6 - Solution heat treated and artificially aged.
 
Fabrication
A:Solderability: Good
B:Weldability - Gas: Excellent
C:Weldability - Arc: Excellent
D:Weldability - Resistance: Excellent
E:Brazability: Excellent
F:Workability - Cold: Average
G:Machinability: Average
 
6063 Aluminum Alloy: Properties

General Characteristics
Characteristic Appraisal
Strength Medium
Corrosion Resistance Good
Weldability & Brazability Good
Workability Good
Machinability Fair

 

Chemical Composition
Element Minimum % Maximum %
Magnesium 0.45 0.9
Silicon 0.2 0.6
Iron No Min 0.35
Copper No Min 0.1
Manganese No Min 0.1
Chromium No Min 0.1
Zinc No Min 0.1
Titanium No Min 0.1
Other Elements No Min 0.05 each, 0.15 in total

 

Physical Properties
Property 6063-T5 6063-T6 6063-T832
Density 2.70 g/cc | 0.0975 lb/in³ 2.70 g/cc | 0.0975 lb/in³ 2.70 g/cc | 0.0975 lb/in³

 

Mechanical Properties
Property 6063-T5 6063-T6 6063-T832
Tensile Strength 186 MPa | 27000 psi 241 MPa | 35000 psi 290 MPa | 42000 psi
Yield Strength 145 MPa | 21000 psi 214 MPa | 31000 psi 269 MPa | 39000 psi
Modulus of Elasticity 68.9 GPa | 10000 ksi 68.9 GPa | 10000 ksi 69.0 GPa | 10000 ksi

 

Thermal Properties
Property 6063-T5 6063-T6 6063-T832
Coefficient of Thermal Expansion @
20.0 - 100 °C Temp
21.8 µm/m-°C | 12.1
µin/in-°F
21.8 µm/m-°C | 12.1
µin/in-°F
21.8 µm/m-°C | 12.1
µin/in-°F
Thermal Conductivity 209 W/m-K | 1450
BTU-in/hr-ft²-°F
200 W/m-K | 1390
BTU-in/hr-ft²-°F
200 W/m-K | 1390
BTU-in/hr-ft²-°F

Aluminum extrusion power amplifier case metal products aluminum shell CNC processing 0Aluminum extrusion power amplifier case metal products aluminum shell CNC processing 1Aluminum extrusion power amplifier case metal products aluminum shell CNC processing 2Aluminum extrusion power amplifier case metal products aluminum shell CNC processing 3Aluminum extrusion power amplifier case metal products aluminum shell CNC processing 4Aluminum extrusion power amplifier case metal products aluminum shell CNC processing 5